Vibsorb Vibration Absorption Bearing pads are a layered rubber and cotton duck fabric bearing that can be used in a wide variety of structural bearing applications. They go by many names such as Fabric Bearings, Preformed Fabric Bearings, Cotton Duck Pads and Cotton Duck Bearings. They can have a sliding surface of PTFE and stainless steel for a Sliding Expansion Bearing or can be plain without sliding surfaces. These bearings are well suited when very little relative rotation can be expected (equal to or less than 0.003 radians) and where they will sustain no more than 2500 psi of compressive stress. 
Except for Sliding Expansion Bearings (where movement is accommodated by the sliding PTFE/Stainless surface), they are not well suited if the movement is expected to be accommodated by shear of the fabric pad.
Vibsorb PTFE-coated anti-vibration pads for heavy machinery - 60% noise reduction with self-lubricating PTFE layer. Made in Canada for industrial durability

Vibsorb Vibration Absorption Pad with PTFE

Vibsorb Vibration MIL C Spec:

The bearing pads shall be manufactured of all new (unused) materials and composed of multiple layers of prestressed 50/50 cotton-polyester blend duck, 8.1 ounce per net square yard, duck warp count 50 ± 1 threads per inch and filling count 40 ± 2 threads per inch, impregnated and bound with a high quality, oil-impervious nitrile rubber compound, containing rot and mildew inhibitors and anti-oxidants, compounded into resilient pads of uniform thickness. The pads shall withstand compressive loads perpendicular to the plane of laminations of not less than 10,000 psi before breakdown

Contact us
Vibsorb Vibration Absorption Bearing pads are a layered rubber and cotton duck fabric bearing that can be used in a wide variety of structural bearing applications. They go by many names such as Fabric Bearings, Preformed Fabric Bearings, Cotton Duck Pads and Cotton Duck Bearings. They can have a sliding surface of PTFE and stainless steel for a Sliding Expansion Bearing or can be plain without sliding surfaces. These bearings are well suited when very little relative rotation can be expected (equal to or less than 0.003 radians) and where they will sustain no more than 2500 psi of compressive stress.
Except for Sliding Expansion Bearings (where movement is accommodated by the sliding PTFE/Stainless surface), they are not well suited if the movement is expected to be accommodated by shear of the fabric pad.
Vibsorb is a high capacity preformed cushioning pad fabricated using multiple layers of high quality cotton polyester duck fabric, completely impregnated with a high-grade nitrile compound. Finished Vibsorb Vibration Absorption pads will withstand compressive loads perpendicular to the plane of laminations of 10,000 pounds minimum per square inch without detrimental reduction in thickness or extrusion.
Benchmark stocks Vibsorb Vibration Absorption Pad pad material the following dimensions in Canada:
Elastomeric Pad Thickness Sheet Dimensions Roll Dimensions
1/16" (1.6mm) 48" (1219mm) x 96" (2438mm) 48" (1219mm) x 300' (91.5 meter)
1/8" (3.2mm) 48" (1219mm) x 96" (2438mm) 48" (1219mm) x 300' (91.5 meter)
15/64" (6mm) 48" (1219mm) x 96" (2438mm) 48" (1219mm) x 300' (91.5 meter)
11/32" (8.8mm) 48" (1219mm) x 96" (2438mm) N/A
1/2" (12.7mm) 48" (1219mm) x 96" (2438mm) N/A
3/4" (19mm) 48" (1219mm) x 96" (2438mm) N/A
1" (25.4mm) 48" (1219mm) x 96" (2438mm) N/A
2" (50.8mm) 48" (1219mm) x 96" (2438mm) N/A
Vibsorb Vibration Absorption Pads are also available in cut to size pieces including holes, slots and other finishing requests. Benchmark also stocks the engineer approved epoxy system for bonding Vibsorb to a variety of surfaces including concrete, steel, PTFE and composite materials.

Physical Properties:

Color: Black with white fabric layers

Finish = Smooth

Elastomer Type = Nitrile

Fabric type = Cotton with Polyester

Fungal resistant

Meets the following Specifications:

D.O.T. Federal Standard Specifications for Construction Administration: of Roads and Bridges on Federal Highway Projects (1985).

AASHTO: Standard Specifications for Highway Bridges.

Preformed Fabric Pads: 16th Edition – 18.10.2 17th Edition – 18.4.9.1 2nd ED.LRFD – 18.10.2

Military Specifications

MIL-C-882, MIL-E-5272A , MIL-STD-810

Vibsorb Vibration Absorption Pad Mechanical Properties

Properties Tested ASTM Test Method Value
Hardness Shore "A" ASTM D2240 90 +- 5
Tensile Strength ASTM D412 5,500 PSI
Ultimate Elongation ASTM D412 600%
Specific Gravity 1.21
Compressive Load 10,000 PSI
Shear Modulus 450 PSI
Modulus of Elasticity 23,000
Temperature Range -20F to +200F
Benchmark accepts no responsibility for individual results obtained. Everyone is strongly recommended to verify data and obtain their own independent test results. This data is subject to change without notice.

PTFE-Faced Isolation Pads, Sliding Bearing Pads, Low-Friction Vibration Pads, Fabreeka-PTFE, Lubrite, Slide Bearings, Slip-joint pads, expansion bearing, bridge slide pads, low-friction mount, Low-Friction Isolation Pad, Slip-Plate Isolator, Anti-Vibration Slide Bearing, Thermal-Vibration Hybrid Pad, Dynamic Load Isolation Mount.

anti vibration pads
vibration isolation pads
industrial vibration pads
machinery vibration isolation
machine vibration isolation pads
rubber vibration isolation pads
neoprene vibration isolation pads
equipment vibration isolation pads
compressor vibration isolation
pump vibration isolation
generator vibration isolation
cooling tower vibration isolation
fan vibration isolation pads
hvac vibration isolation pads
structure borne noise isolation
vibration isolation mounts
vibration control mounts
vibration isolation bushings
vibration isolation washers
shock isolation pads
industrial shock absorption pads
mil c 882 vibration pads